| About |
|---|
| Celanex 3300SW1 is a 30% glass filled PBT with excellent wear characteristics.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Good wear resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.61 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 250℃，2.16kg | 17 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.70 to 0.90 | % | |
| MD | 0.30 to 0.50 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 50 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 212 | ℃ | ISO 75-2/A |
| Melting temperature | 224 | ℃ | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 88 | ISO 2039-2 | |
| Tensile modulus | 9600 | MPa | ISO 527-2/1A |
| tensile strength | |||
| fracture | 125 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 2.8 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 8950 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 195 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |