Celcon® UV90Z

About
Celcon® UV90Z is an integrally colored nominal 9 melt flow rate based acetal copolymer material stabilized for use where ultraviolet radiation exposure is to be encountered. The material is formulated to prevent discoloration, fading, chalking and mechanical property change in severe ultraviolet exposure. This product is available in many colors formulated for the interior automotive market and other applications.&&

About

Celcon® UV90Z is an integrally colored nominal 9 melt flow rate based acetal copolymer material stabilized for use where ultraviolet radiation exposure is to be encountered. The material is formulated to prevent discoloration, fading, chalking and mechanical property change in severe ultraviolet exposure. This product is available in many colors formulated for the interior automotive market and other applications.&&

Product Description
Supplier	Celanese
Generic	Copolymer Polyformaldehyde
Material Status	Commercial: Active
Features	Weather resistance is good
Availabilitys	North America,Latin America,Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.41	g/cm³	ASTM D792
Density	1.41	g/cm³	ISO 1183
Melt Volume Rate
190℃，2.16 kg	8.00	cm³/10min	ISO 1133
Shrinkage rate			ISO 294-4
TD	1.8	%	ASTM D955
MD	2.2	%	ASTM D955
TD	1.7	%	ISO 294-4
MD	1.9	%	ISO 294-4
Water absorption rate
Saturation, 23 ℃	0.75	%	ISO 62
Equilibrium, 23 ℃, 50% RH	0.20	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	2700	MPa	ISO 527-2/1A/1
tensile strength
Yield, 23 ℃	60.7	MPa	ASTM D638
yield	64.0	MPa	ISO 527-2/1A/50
Tensile strain
yield	9.0	%	ISO 527-2/1A/50
Bending modulus
23℃	2470	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	6.0	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength
23℃	100	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch
23℃	5.7	kJ/m²	ISO 180-1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	110	℃	ASTM D648
1.8 MPa, unannealed	91.0	℃	ISO 75-2/A
0.45 MPa, unannealed	155	℃	ISO 75-2/B
Melting peak temperature	165	℃	ASTM D3418
Melting temperature	165	℃	ISO 11357-3
Linear coefficient of thermal expansion
TD	1.2E-4	1/℃	ISO 11359-2
MD	1.1E-4	1/℃	ISO 11359-2

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80 to 100	°C
Drying time	3.0	hr
Barrel rear temperature	170 to 180	°C
Barrel middle temperature	180 to 190	°C
Barrel front temperature	180 to 190	°C
Nozzle temperature	190 to 200	°C
Processing (melt) temperature	180 to 200	°C
Mold temperature	80 to 120	°C
Injection pressure	60.0 to 120	MPa
Injection speed	Slow-Moderate
Hold pressure	60.0 to 120	MPa
Back pressure	0.00 to 4.00	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.