| CELEX™ 500S2 PC/ABS alloy is designed with easy processing. Applications: Automotive instrument panels Automotive interior/exterior trims Small appliance and electrical applications&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 4.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.20 mm, injection molding | 50.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm, injection molded | 24 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2390 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 77.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 490 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 102 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 83.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm, natural color, white, red | HB | UL 94 | |
| 1.20 mm, all colors | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 210 to 230 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |