| About |
|---|
| CELEX 5200HF.K is a non-halogen ignition resistant PC/ABS alloy. It combines the superior physical properties of PC and the excellent processability of ABS. Applications: ITE enclosures Instrument panel&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Halogen free,Flame Characteristics,V-0,5VB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 18 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 3.20 mm, injection molded | 2450 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 3.20 mm, injection molding | 55.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm, injection molded | 100 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2600 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 88.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20 ℃, 3.2mm, injection molding | 220 | J/m | ASTM D256 |
| 23 ℃, 3.2mm, injection molding | 750 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 76.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 100 | ℃ | ASTM D1525 3 |
| Relative temperature index | 60.0 | ℃ | UL 746 |
| Electrical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+11 | ohms·cm | ASTM D257 |
| Dielectric strength | 26 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | > 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.40 mm | V-0 | UL 94 | |
| 1.50 mm | 5VB | UL 94 | |
| Glowing wire flammability index | |||
| 1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1.5 mm | 750 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 190 to 220 | °C | |
| Barrel middle temperature | 200 to 225 | °C | |
| Barrel front temperature | 205 to 235 | °C | |
| Nozzle temperature | 210 to 235 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h), Loading 1 (10 N) |
| 3. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |