| About |
|---|
| 50 % Long glass fiber reinforced, heat stabilized, Nylon 6/6&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.56 | g/cm³ | ASTM D792 |
| Density | 1.56 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.15 to 0.25 | % | ASTM D955 |
| MD | 0.10 to 0.15 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ASTM D638 | ||
| -40℃ | 19800 | MPa | ASTM D638 |
| 23℃ | 18300 | MPa | ASTM D638 |
| 149℃ | 12400 | MPa | ASTM D638 |
| Tensile modulus | 17000 | MPa | ISO 527-2/1A/1 |
| tensile strength | ASTM D638 | ||
| fracture | 265 | MPa | ISO 527-2/1A/5 |
| Fracture, -40 ℃ | 343 | MPa | ASTM D638 |
| Fracture, 23 ℃ | 299 | MPa | ASTM D638 |
| Fracture, 149 ℃ | 153 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| fracture | 2.0 | % | ISO 527-2/1A/5 |
| Fracture, -40 ℃ | 2.1 | % | ASTM D638 |
| Fracture, 23 ℃ | 2.2 | % | ASTM D638 |
| Fracture, 149 ℃ | 2.4 | % | ASTM D638 |
| Bending modulus | ISO 178 | ||
| 23℃ | 15000 | MPa | ISO 178 |
| 80℃ | 9000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 415 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 34 | kJ/m² | ISO 179/1eA |
| 23℃ | 47 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 80 | kJ/m² | ISO 179/1eU |
| 23℃ | 95 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 8.0 MPa, unannealed | 249 | ℃ | ISO 75-2/C |
| 1.8 MPa, unannealed | 260 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 256 | ℃ | ISO 75-2/A |
| Melting temperature | 261 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 to 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.18 | % | |
| Hopper temperature | 70 to 80 | °C | |
| Barrel rear temperature | 285 to 295 | °C | |
| Barrel middle temperature | 290 to 300 | °C | |
| Barrel front temperature | 300 to 310 | °C | |
| Nozzle temperature | 300 to 315 | °C | |
| Processing (melt) temperature | 300 to 315 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |