Celstran® PA66-GF50-07

About
50% long fiber glass reinforced, enhanced flow, Nylon 6/6&&

Product Description
Supplier	Celanese
Generic	PA66
Material Status	Commercial: Active
Features	Good liquidity
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.56	g/cm³	ISO 1183

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	16600	MPa	ISO 527-2/1A/1
tensile strength
fracture	230	MPa	ISO 527-2/1A/5
Tensile strain
fracture	1.8	%	ISO 527-2/1A/5
Bending modulus
23℃	15000	MPa	ISO 178
bending strength
23℃	360	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	33	kJ/m²	ISO 179/1eA

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	70 to 80	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.18	%
Hopper temperature	70 to 80	°C
Barrel rear temperature	285 to 295	°C
Barrel middle temperature	290 to 300	°C
Barrel front temperature	300 to 310	°C
Nozzle temperature	300 to 315	°C
Processing (melt) temperature	300 to 315	°C
Mold temperature	80 to 100	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.