Celstran® PA66-GF60-02 AD3002 Black

About
Material code according to ISO 1043-1: PA66 Heat stabilized Nylon 66 reinforced by 60 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.&&

About

Material code according to ISO 1043-1: PA66 Heat stabilized Nylon 66 reinforced by 60 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.&&

Product Description
Supplier	Celanese
Generic	PA66
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,Heat Stabilized
Availabilitys	North America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	21200	MPa
tensile strength
fracture	255	MPa
Tensile strain
fracture	1.5	%
Bending modulus
23℃	19000	MPa
bending strength
23℃	410	MPa

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	53	kJ/m²

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	70 to 80	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.15	%
Hopper temperature	70 to 80	°C
Barrel rear temperature	275 to 285	°C
Barrel middle temperature	285 to 295	°C
Barrel front temperature	295 to 305	°C
Processing (melt) temperature	315 to 325	°C
Mold temperature	90 to 120	°C
Injection speed	中等
Back pressure	< 3.00	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.