Celstran® POM-GF25-04 AF3001

About
Material code according to ISO 1043-1: POM Acetal copolymer reinforced with 25 weight percent long glass fibers. The fibers are chemically coupled to the POM matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive&&

About

Material code according to ISO 1043-1: POM Acetal copolymer reinforced with 25 weight percent long glass fibers. The fibers are chemically coupled to the POM matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive&&

Product Description
Supplier	Celanese
Generic	Copolymer Polyformaldehyde
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,High impact resistance,Chemical coupling,Copolymer,low-temperature impact resistance
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.59	g/cm³	ISO 1183

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	10300	MPa	ISO 527-2/1A/1
tensile strength
fracture	177	MPa	ISO 527-2/1A/5
Tensile strain
fracture	2.4	%	ISO 527-2/1A/5
Bending modulus
23℃	9190	MPa	ISO 178
bending strength
23℃	265	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	35	kJ/m²	ISO 179/1eA

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80 to 90	°C
Drying time	3.0	hr
Recommended maximum moisture content	0.15	%
Barrel rear temperature	180 to 195	°C
Barrel middle temperature	190 to 200	°C
Barrel front temperature	195 to 205	°C
Nozzle temperature	195 to 205	°C
Processing (melt) temperature	195 to 205	°C
Mold temperature	70 to 110	°C
Injection pressure	60.0 to 120	MPa
Injection speed	中等
Hold pressure	60.0 to 120	MPa
Back pressure	0.00 to 3.00	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.