| 30% long fiber glass reinforced, enhanced flow, UV stabilized, Polypropylene&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good liquidity |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6360 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 96.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 2.2 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 6500 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 165 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 20 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 157 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 161 | ℃ | ISO 75-2/B |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 2.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 200 to 205 | °C | |
| Barrel middle temperature | 210 to 215 | °C | |
| Barrel front temperature | 215 to 220 | °C | |
| Nozzle temperature | 220 to 225 | °C | |
| Processing (melt) temperature | 220 to 225 | °C | |
| Mold temperature | 40 to 70 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |