| About |
|---|
| 40% long strand glass fiber reinforced thermoplastic polyurethane&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | TPU |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.52 | g/cm³ | ASTM D792 |
| Density | 1.52 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.10 to 0.20 | % | ASTM D955 |
| MD | 0.050 to 0.10 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11100 | MPa | ISO 527-2/1A/1 |
| 23℃ | 12100 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 23 ℃ | 233 | MPa | ASTM D638 |
| fracture | 210 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.6 | % | ASTM D638 |
| fracture | 2.5 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 10100 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 315 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 48 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 34 | kJ/m² | ISO 180-1A |
| 23℃ | 39 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 90.0 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 90.6 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Hopper temperature | 70 to 80 | °C | |
| Barrel rear temperature | 240 to 250 | °C | |
| Barrel middle temperature | 245 to 255 | °C | |
| Barrel front temperature | 245 to 260 | °C | |
| Nozzle temperature | 245 to 260 | °C | |
| Processing (melt) temperature | 245 to 260 | °C | |
| Mold temperature | 70 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |