CERTENE™ HWF-0852

About
HWF-0852 is a certified High Molecular Weight Hexene copolymer grade, developed for production of thin-gauged high stiffness paper-like blown films. HWF-0852 features BIMODAL and BROAD molecular weight distribution which greatly improve processability in HDPE blow film equipment, offers outstanding film mechanical properties and high film drawdown. HWF-0852 applications include shoppers, grocery bags, merchant and produce bags, refuse sacks, single and multiwall liners, lamination and meat & cheese wrap films, and as substitute films for grease-proof waxed and acid free papers. Minimum recommended film gauge is 0.5 mil, and melt processing temperature between 210 to 230°C.&&

About

HWF-0852 is a certified High Molecular Weight Hexene copolymer grade, developed for production of thin-gauged high stiffness paper-like blown films. HWF-0852 features BIMODAL and BROAD molecular weight distribution which greatly improve processability in HDPE blow film equipment, offers outstanding film mechanical properties and high film drawdown. HWF-0852 applications include shoppers, grocery bags, merchant and produce bags, refuse sacks, single and multiwall liners, lamination and meat & cheese wrap films, and as substitute films for grease-proof waxed and acid free papers. Minimum recommended film gauge is 0.5 mil, and melt processing temperature between 210 to 230°C.&&

Product Description
Generic	HDPE
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,Wide molecular weight distribution,Food contact compliance,Copolymer,Grease resistance
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.952	g/cm³	ASTM D1505
Melt Flow Rate			ASTM D1238
190℃，2.16kg	0.050	g/10min	ASTM D1238
190℃，21.6kg	8.0	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
film thickness
test	13	µm
Secant modulus
1% secant, TD	965	MPa	ASTM D882
1% secant, MD	790	MPa	ASTM D882
tensile strength
TD, fracture	41.0	MPa	ASTM D882
TD, yield	26.0	MPa	ASTM D882
MD, fracture	69.0	MPa	ASTM D882
MD, yield	28.0	MPa	ASTM D882
Tensile strain
TD, fracture	480	%	ASTM D882
MD, fracture	330	%	ASTM D882
Drop hammer impact	280	g	ASTM D1709-A
Elmandorf tear strength
MD	20	g	ASTM D1922
tear strength
TD	200	g	ASTM D1922

THERMAL	Nominal value	Unit	Test method
Melting peak temperature	129	℃	ASTM D3417

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	210 to 230	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.