| LLBF-218A is a certified prime resin with Butene-comonomer designed for production of Cast or Blown film for Stretch-Cling and General Purpose applications. LLBF-218A features easy processability, good film strength and a broad heat sealing range. LLBF-218A major applications include stretch-cling, garment bags, produce bags and liners. LLBF-218A contains no slip and no antiblock. LLBF-218A complies with FDA regulation 21CFR 177.1520(c) 3.1a.&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good heat sealing,Butylene copolymer |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | |||
| 1% secant, TD, 25 µ m | 186 | MPa | ASTM D882 |
| 1% secant, MD, 25 µ m | 172 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture, 25 µ m | 25.0 | MPa | ASTM D882 |
| TD, yield, 25 µ m | 10.0 | MPa | ASTM D882 |
| MD, fracture, 25 µ m | 32.0 | MPa | ASTM D882 |
| MD, yield, 25 µ m | 10.0 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 25 µ m | 700 | % | ASTM D882 |
| MD, fracture, 25 µ m | 650 | % | ASTM D882 |
| Drop hammer impact | |||
| 25 µm | 95 | g | ASTM D1709-A |
| Elmandorf tear strength | |||
| MD，25 µm | 100 | g | ASTM D1922 |
| tear strength | |||
| TD，25 µm | 350 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 40 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 14 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |