| About |
|---|
| PHP-1 is a certified prime grade Polypropylene specially designed for PROFILE EXTRUSION. PHP-1 combines excellent processability, enhanced Long-Term Thermal Stability. PHP-1 applications include PROFILES AND FLAT and CORRUGATED SHEET. PHP-1 complies with FDA regulation 21CFR 177.1520 and with most international regulations concerning the use of Polypropylene in contact with food articles.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Food contact compliance,Heat Stabilized |
| Availabilitys | North America,Latin America |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.50 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 69 | J/m | ASTM D256-A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 101 | ASTM D785 | |
| tensile strength | |||
| yield | 33.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 13 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 1380 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Test made on injection molded Type 1 tension test specimen according to ASTM D 2146. |
| 4. 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |