| About |
|---|
| Product Description | |
|---|---|
| Supplier | Daicel |
| Generic | MMS |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 13 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.30 to 0.50 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.15 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 2.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 15 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 12.7 mm | 90.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 80.0 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | ISO 11359-2 |
| Ball pressure test | 90 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 80 | ISO 2039-2 | |
| tensile strength | |||
| yield | 70.0 | MPa | ISO 527-2 |
| Bending modulus | 3400 | MPa | ISO 178 |
| bending strength | 115 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 to 85 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Temperature at the rear of the barrel | 170 to 190 | °C | |
| Temperature in the middle of the barrel | 190 to 210 | °C | |
| Front temperature of material barrel | 210 to 230 | °C | |
| Nozzle temperature | 210 to 230 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Back pressure | 10.0 to 20.0 | MPa | |
| Screw speed | 70 to 90 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |