| About |
|---|
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Volume Rate | |||
| 300°C/1.2 kg | 6 | cm³/10min | ISO 1133 |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Tensile molding shrinkage rate | |||
| flow | 0.5 – 0.7 | % | SABIC 方法 |
| Water absorption rate | |||
| 23 ° C, saturated | 0.35 | % | ISO 62-1 |
| 23°C/50% RH | 0.15 | % | ISO 62 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 2.54mm | ＜0.8 | % | ASTM D1003 |
| Transmittance | |||
| 2.54mm | 88 – 90 | % | ASTM D1003 |
| Refractive index | 1.586 | ISO 489 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃，80*10*3 | NB | KJ/m² | ISO 180/1U |
| -30℃，80*10*3 | NB | KJ/m² | ISO 180/1U |
| Impact strength of cantilever beam notch | |||
| 23℃，80*10*3 | 70 | KJ/m² | ISO 180/1A |
| -30℃，80*10*3 | 12 | KJ/m² | ISO 180/1A |
| Charpy Notched Impact Strength | |||
| 23℃，V-notch Edgew 80*10*3 sp=62mm | 75 | kJ/m² | ISO 179/1eA |
| -30℃，V-notch Edgew 80*10*3 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
| 23℃ | 35 | kJ/m² | ISO 179/2C |
| Charpy Unnotch Impact strength | |||
| 23℃，V-notch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| -30℃，V-notch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Wear resistance test | |||
| CS-17, 1kg | 10 | mg/1000cy | SABIC 方法 |
| Tensile stress | |||
| Yield, 50 mm/min | 63 | MPa | ISO 527 |
| Fracture, 50 mm/min | 70 | MPa | ISO 527 |
| Tensile strain | |||
| Yield, 50 mm/min | 6 | % | ISO 527 |
| Nominal fracture strain | |||
| 50 mm/min | 120 | % | ISO 527 |
| Tensile modulus | |||
| 1 mm/min | 2350 | MPa | ISO 527 |
| Bending stress | |||
| Yield, 2 mm/min | 90 | MPa | ISO 178 |
| Elastic modulus | |||
| 2 mm/min | 2300 | MPa | ISO 178 |
| Ball hardness | |||
| H358/30 | 95 | MPa | ISO 2039-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermal conductivity coefficient | 0.2 | W/m-℃ | ISO 8302 |
| Linear coefficient of thermal expansion | |||
| 23 ° C~80 ° C, flowing | 7.0 | ×10-5/℃ | ISO 11359-2 |
| Ball pressure test | |||
| 125±2℃ | 通过 | IEC 60695-10-2 | |
| Approximately maximum value | 140 | IEC 60695-10-2 | |
| Vicat Softening Temp | |||
| B/50 | 144 | ℃ | ISO 306 |
| B/120 | 145 | ℃ | ISO 306 |
| Hot deformation temperature | |||
| 0.45 MPa Flatw 80*10*4 sp=64mm | 138 | ℃ | ISO 75/Be |
| 1.80 MPa Flatw 80*10*4 sp=64mm | 127 | ℃ | ISO 75/Ae |
| Relative temperature index | |||
| Electrical characteristics | 130 | ℃ | UL-746B |
| Mechanical impact characteristics | 130 | ℃ | UL-746B |
| Non mechanical impact characteristics | 130 | ℃ | UL-746B |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | ＞E+15 | ohm·cm | IEC 60093 |
| Surface resistivity | ＞E+15 | ohm | IEC 60093 |
| Dielectric strength | |||
| In oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 50/60 Hz | 2.7 | IEC 60250 | |
| 1 MHz | 2.7 | IEC 60250 | |
| Dissipation factor | |||
| 50/60 Hz | 0.001 | IEC 60250 | |
| 1 MHz | 0.01 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| UL certified 94HB flame retardant rating | |||
| 0.75 | mm | UL94 | |
| 3 | mm | UL94 | |
| Glowing wire flammability index | |||
| 850℃ | 1 | mm | IEC 60695-2-12 |
| Extreme oxygen index | 25 | % | ISO 4589 |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| drying temperature | 120 | ℃ | |
| Drying time | 2 – 4 | hr | |
| Maximum moisture content | 0.02 | % | |
| Melting temperature | 290 – 320 | ℃ | |
| Mouth temperature | 280 – 310 | ℃ | |
| Front temperature | 290 – 320 | ℃ | |
| Mid section temperature | 280 – 310 | ℃ | |
| Post stage temperature | 270 – 300 | ℃ | |
| Hopper temperature | 60 – 80 | ℃ | |
| Mold temperature | 80 – 120 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |