| About |
|---|
| Chemlon® 100 H is a Polyamide 66 (Nylon 66) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Chemlon® 100 H are: Flame Rated Good Processability Good Toughness Heat Stabilizer High Strength Typical applications include: Automotive Appliances Electrical/Electronic Applications Wire & Cable&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Heat Stabilized,Good Rigidity,Excellent Processability,V-2,Lubricating |
| Availabilitys | Europe,Asia Pacific,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 3105 | MPa | ISO 527 |
| Tensile Strength | 82.11 | MPa | ISO 527-2 |
| Flexural Modulus | 2904.9 | MPa | ISO 178 |
| Flexural Strength | 100.05 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 3.78 | kJ/m² | ISO 179 |
| 23℃ | 4.41 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.82 MPa | 84 | ℃ | ISO 75-1/-2 |
| Melting temperature | 259 | ℃ | ISO 11357-3 |
| Coeff. of linear thermal expansion | |||
| Flowing flow | 3.9E-5E | in/in/℉ | ISO 11359-2 |
| Relative Temperature Index (RTI) | |||
| Elec | |||
| 0.8 mm | 130 | ℃ | UL-746B |
| 1.6 mm | 130 | ℃ | UL-746B |
| 3.2 mm | 130 | ℃ | UL-746B |
| Imp | |||
| 0.8 mm | 95 | ℃ | UL-746B |
| 1.6 mm | 105 | ℃ | UL-746B |
| 3.2 mm | 110 | ℃ | UL-746B |
| Str | |||
| 0.8 mm | 110 | ℃ | UL-746B |
| 1.6 mm | 110 | ℃ | UL-746B |
| 3.2 mm | 110 | ℃ | UL-746B |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 1E14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 460 | V/mil | ASTM D149 |
| Compared Tracking Index | 600 | V | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning Speed | <3.9 | in/min | ISO 3795 |
| Flame Class Rating | |||
| 0.8 mm | V-2 | UL 94 | |
| Oxygen Index | 27 | % | ASTM D2863 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 79 | °C | |
| Maximum Moisture Content | 0.20 | % | |
| Suggested maximum proportion of recycled materials | 25 | % | |
| Rear Temperature Zone 1 | 241 to 254 | °C | |
| Middle Temperature Zone 2 | 257 to 271 | °C | |
| Front Temperature Zone 3 | 263 to 282 | °C | |
| Nozzle temperature | 263 to 279 | °C | |
| Melt Temperature | 263 to 279 | °C | |
| Mold Temperature | 21 to 93 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Screw Speed | 60 to 120 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |