| Chemlon® 100 L is a Polyamide 66 (Nylon 66) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Chemlon® 100 L are: Flame Rated Lubricated&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Lubricating,V-2 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 235℃，1.0kg | 10 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 1.5 to 2.2 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 1.2 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 82.7 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| yield | 5.0 | % | |
| fracture | 50 | % | |
| Bending modulus | 2790 | MPa | ASTM D790 |
| bending strength | 109 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 53 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 218 | ℃ | |
| 1.8 MPa, unannealed | 87.8 | ℃ | |
| Melting temperature | 257 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD | 7.1E-5 | 1/℃ | ASTM D696 |
| Relative temperature index | UL 746 | ||
| Electrical performance | UL 746 | ||
| 0.810 mm | 115 | ℃ | |
| 1.50 mm | 115 | ℃ | |
| 3.00 mm | 115 | ℃ | |
| Impact mechanical performance | UL 746 | ||
| 0.810 mm | 75.0 | ℃ | |
| 1.50 mm | 75.0 | ℃ | |
| 3.00 mm | 85.0 | ℃ | |
| 0.81 mm | 95.0 | ℃ | |
| 1.50 mm | 95.0 | ℃ | |
| 3.00 mm | 95.0 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3 mm | 18 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | 600 | V | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.81 mm | V-2 | UL 94 | |
| Extreme oxygen index | 27 | % | ASTM D2863 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 79.4 | °C | |
| Recommended maximum moisture content | 0.20 | % | |
| Suggested maximum proportion of recycled materials | 25 | % | |
| Temperature at the rear of the barrel | 241 to 254 | °C | |
| Temperature in the middle of the barrel | 257 to 274 | °C | |
| Front temperature of material barrel | 263 to 282 | °C | |
| Nozzle temperature | 263 to 279 | °C | |
| Processing (melt) temperature | 263 to 279 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |