| About |
|---|
| Chemlon® 109 H is a Polyamide 66 (Nylon 66) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Chemlon® 109 H are: Flame Rated Impact Resistant Good Processability Good Toughness Heat Stabilizer Typical application of Chemlon® 109 H: Automotive&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good flexibility,HB,High impact resistance,Heat Stabilized,low-temperature impact resistance,Good Rigidity,Excellent Processability |
| Availabilitys | Europe,Asia Pacific,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ISO 1183 |
| Molding shrinkage | |||
| Cross flow | 1.9 | % | ISO 294-4 |
| Flowing flow | 2.0 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| Dry | 2001 | MPa | ISO 527 |
| Wet Cond | 807.3 | MPa | ISO 527 |
| Tensile Strength | |||
| Dry | 44 | MPa | ISO 527-2 |
| Wet Cond | 40 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK, dry dry | 77 | % | ISO 527 |
| Broken BRK, wet Cond | 200 | % | ISO 527 |
| Flexural Modulus | |||
| Dry | 1752.6 | MPa | ISO 178 |
| Wet Cond | 765.9 | MPa | ISO 178 |
| Flexural Strength | |||
| Dry | 52 | MPa | ISO 178 |
| Wet Cond | 22 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30 ℃, dry | 17.01 | kJ/m² | ISO 179 |
| -30 ℃, moist cond | 109.2 | kJ/m² | ISO 179 |
| 23 ℃, dry | 79.8 | kJ/m² | ISO 179 |
| 23 ℃, moist cond | 109.2 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| Dry | 84 | kJ/m² | ISO 179 |
| Wet Cond | NB | kJ/m² | ISO 179 |
| Izod Notched Impact strength | |||
| Dry | 67.2 | KJ/m² | ISO 180/1A |
| Wet Cond | 94.5 | KJ/m² | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa | 122 | ℃ | ISO 75-1/-2 |
| 1.82 MPa | 60 | ℃ | ISO 75-1/-2 |
| Melting temperature | 257 | ℃ | ISO 11357-3 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 1E13 | ohms·cm | ASTM D257 |
| Dielectric Strength | |||
| 3.0 mm | 250 | V/mil | ASTM D149 |
| Compared Tracking Index | 600 | V | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.8 mm | HB | UL 94 | |
| Oxygen Index | 21 | % | ASTM D2863 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion Molded | Nominal value | Unit | Test method |
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 80 | ℃ | |
| Maximum Moisture Content | 0.2 | % | |
| Melt Temperature | 265-293 | ℃ | |
| Die Temperature | 265-293 | ℃ | |
| Screw L/D Ratio | 25.0:1.0-30.0:1.0 | ||
| Drying Temperature | 80 | ℃ | |
| Maximum Moisture Content | 0.2 | % | |
| Melt Temperature | 265-293 | ℃ | |
| Mold Temperature | 77-88 | ℃ | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |