| About |
|---|
| 60GS6 is a 30% glass sphere filled nylon 6.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Europe,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding shrinkage | 0.6-1.5 | % | Internal Method |
| Water Absorption | |||
| Equilibrium, 23 ℃, 50% r. h | 2.0 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| Dry | 3505.2 | MPa | ISO 527 |
| Wet Cond | 1704.3 | MPa | ISO 527 |
| Tensile Strength | |||
| Broken BRK, dry dry | 80.04 | MPa | ISO 527-2 |
| Broken BRK, wet Cond | 40.02 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK, dry dry | 10 | % | ISO 527 |
| Broken BRK, wet Cond | 20-50 | % | ISO 527 |
| Flexural Modulus | |||
| Dry | 2504.7 | MPa | ISO 178 |
| Wet Cond | 1000.5 | MPa | ISO 178 |
| Flexural Strength | |||
| Dry | 124.89 | MPa | ISO 178 |
| Wet Cond | 60.03 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| Dry | 6.51 | kJ/m² | ISO 179 |
| Wet Cond | 11.97 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | 37.8 | kJ/m² | ISO 179 |
| Izod Notched Impact strength | 3.99 | KJ/m² | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa, dry | 205 | ℃ | ISO 75-1/-2 |
| 0.45 MPa, wet cond | 185 | ℃ | ISO 75-1/-2 |
| 1.82 MPa, dry | 70 | ℃ | ISO 75-1/-2 |
| 1.82 MPa, wet cond | 65 | ℃ | ISO 75-1/-2 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface Resistivity | |||
| Dry | 1E14 | ohms | IEC 60093 |
| Wet Cond | 1E11 | ohms | IEC 60093 |
| Volume Resistance | |||
| Dry | 1E16 | ohms·cm | IEC 60093 |
| Wet Cond | 1E14 | ohms·cm | IEC 60093 |
| Electric strength | |||
| Dry | 280 | V/mil | IEC 60243-1 |
| Wet Cond | 200 | V/mil | IEC 60243-1 |
| Relative permittivity | |||
| Dry | 3.8 | IEC 60250 | |
| Wet Cond | 4.2 | IEC 60250 | |
| Compared Tracking Index | |||
| Dry | 600 | V | IEC 60112 |
| Wet Cond | 500 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.8 mm | HB | UL 94 | |
| Oxygen Index | 24 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 80 | ℃ | |
| Drying Time | 2.0 | hr | |
| Rear Temperature Zone 1 | 230-280 | ℃ | |
| Middle Temperature Zone 2 | 230-280 | ℃ | |
| Front Temperature Zone 3 | 230-280 | ℃ | |
| Melt Temperature | <300 | ℃ | |
| Mold Temperature | 60-80 | ℃ | |
| Injection Rate | 快速 | ||
| Screw Speed | 50-200 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| 3. Yield |
| 4. Break |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |