| Clariant ABS ABS5400 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in North America for injection molding. Important attributes of Clariant ABS ABS5400 are: Chemical Resistant Good Dimensional Stability High Gloss Impact Resistant UV Resistant&& |
| Product Description | |
|---|---|
| Supplier | Clariant |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,High impact resistance,Good Dimensional Stability,Solvent resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.35 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 210 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 103 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 90.6 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 8.8E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 17 | kV/mm | ASTM D149 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 106 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| fracture | 45.5 | MPa | ASTM D638 |
| — | 45.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 25 | % | ASTM D638 |
| Bending modulus | 2280 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 204 to 249 | °C | |
| Barrel middle temperature | 204 to 249 | °C | |
| Barrel front temperature | 204 to 249 | °C | |
| Processing (melt) temperature | 204 to 246 | °C | |
| Melt temperature (target) | 227 | °C | |
| Mold temperature | 24 to 79 | °C | |
| Injection speed | 快速 | ||
| Back pressure | 0.345 to 2.07 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Cushion | 3.18 to 6.35 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |