| Clariant Nylon 6/6 6601-LN is a Polyamide 66 (Nylon 66) material. It is available in North America for injection molding. Important attributes of Clariant Nylon 6/6 6601-LN are: Fast Molding Cycle Good Mold Release Lubricated&& |
| Product Description | |
|---|---|
| Supplier | Clariant |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Nucleation,Quick molding cycle,Good stripping performance,Lubricating |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 1.4 to 1.9 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 75.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 20 | % | ASTM D638 |
| Bending modulus | 2760 | MPa | ASTM D790 |
| bending strength | 110 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 48 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 82.2 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 227 | ℃ | ASTM D648 |
| Melting temperature | 259 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 to 82 | °C | |
| Proposed maximum recycled material ratio | 25 | % | |
| Barrel rear temperature | 249 to 266 | °C | |
| Barrel middle temperature | 271 to 288 | °C | |
| Barrel front temperature | 282 to 293 | °C | |
| Nozzle temperature | 266 to 288 | °C | |
| Mold temperature | 54 to 93 | °C | |
| Injection pressure | 34.5 to 103 | MPa | |
| Back pressure | 0.00 to 5.52 | MPa | |
| Screw speed | 30 to 90 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |