| About |
|---|
| Clariant Nylon 6/6 6604G43-L是一种聚酰胺66（尼龙66）材料,含有的填充物为43% 玻璃纤维增强材料。 该产品在北美洲有供货,加工方式为:注射成型。 Clariant Nylon 6/6 6604G43-L的主要特性有: 冲击改性 润滑&& |
| Product Description | |
|---|---|
| Supplier | Clariant |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | High impact resistance,Lubricating |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.50 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 124 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 7580 | MPa | ASTM D790 |
| bending strength | 165 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 100 | J/m | ASTM D256 |
| Tensile impact strength | 34.7 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 241 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 249 | ℃ | ASTM D648 |
| Melting temperature | 259 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 to 82 | °C | |
| Proposed maximum recycled material ratio | 25 | % | |
| Barrel rear temperature | 249 to 271 | °C | |
| Barrel middle temperature | 271 to 288 | °C | |
| Barrel front temperature | 282 to 299 | °C | |
| Nozzle temperature | 266 to 288 | °C | |
| Mold temperature | 71 to 104 | °C | |
| Injection pressure | 55.2 to 138 | MPa | |
| Back pressure | 0.00 to 1.03 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |