| About |
|---|
| Clariant Nylon 6 PA-211GF30 TF15 is a Polyamide 6 (Nylon 6) material filled with 30% glass fiber. It is available in North America for injection molding. Important attributes of Clariant Nylon 6 PA-211GF30 TF15 are: Flame Rated Chemical Resistant Corrosion Resistant Flame Retardant Good Dimensional Stability Typical applications include: Engineering/Industrial Parts Medical/Healthcare Military Applications Sporting Goods Wire & Cable&& |
| Product Description | |
|---|---|
| Supplier | Clariant |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,Good Dimensional Stability,Low coefficient of friction,Corrosion Resistant,Flame Characteristics,Lubricating,Good wear resistance,Solvent resistance,Good coloring,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.49 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.85 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 204 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 213 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 3.6E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | 20 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 131 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 8620 | MPa | ASTM D790 |
| bending strength | 228 | MPa | ASTM D790 |
| Rockwell hardness | ASTM D785 | ||
| M-level | 88 | ASTM D785 | |
| R-level | 123 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 79 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 249 to 274 | °C | |
| Barrel middle temperature | 249 to 274 | °C | |
| Barrel front temperature | 249 to 274 | °C | |
| Processing (melt) temperature | 254 to 271 | °C | |
| Melt temperature (target) | 266 | °C | |
| Mold temperature | 66 to 93 | °C | |
| Injection speed | Fast | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Cushion | 3.18 to 6.35 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |