| About |
|---|
| Developed with our unique polymerization technology, Cleapact is a type of styrene copolymer resin that excels in the balance of transparency, shock-resistance and molding capacity. Products in this category have a variety of positive characteristics and meet diverse range of user needs.&& |
| Product Description | |
|---|---|
| Supplier | DIC Corporation |
| Generic | SBC |
| Material Status | Commercial: Active |
| Features | Good Clarity,noise reduction,Food contact compliance,HB |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Flow Rate | 3.5 | g/10min | ISO 1133 |
| Shrinkage rate | 0.30 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| injection molding | 10 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 85.0 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| injection molding | 89.0 | % | JIS K7105 |
| Haze | |||
| Injection molded film | 2.5 | % | JIS K7105 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| Level L | 69 | ISO 2039-2 | |
| tensile strength | ISO 527-2 | ||
| Yield, injection molding | 47.0 | MPa | ISO 527-2 |
| Fracture, injection molding | 33.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, injection molding | 15 | % | ISO 527-2 |
| Bending modulus | |||
| injection molding | 2430 | MPa | ISO 178 |
| bending strength | |||
| injection molding | 71.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 75 | °C | |
| Drying time | 3.0 | hr | |
| Drying temperature | 75 | °C | |
| Drying time | 3.0 | hr | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |