| About |
|---|
| Clearflex FF 506 is an hexene copolymer linear medium density polyethylene (C6-LMDPE), with antioxidants and processing aid, suitable for blown film extrusion. Film manufactured with Clearflex FF 506 are characterized by high rigidity and temperature resistance, good sealing properties. Main Applications Clearflex FF 506 is characterized by good mechanical and sealing performances, it is recommended for applications in which the high rigidity of this resin is a key factor (hygienic film and packaging for mineral water). The high Vicat softening point makes Clearflex FF 506 ideal for the production of film for food which is submitted to pasteurisation or sterilisation process.&& |
| Product Description | |
|---|---|
| Generic | LMDPE |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Good heat sealing,Food contact compliance,High Heat Resistance,Inoxidizability,Hexene copolymers |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.934 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.75 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Dynamic, blow molded film | > 0.50 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| film thickness | 10 to 50 µm | ||
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, 25 µ m, blow molded film | 400 | MPa | ISO 527-3 |
| 1% secant, TD, 25 µ m, blow molded film | 450 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 25 µ m, blow molded film | 16.0 | MPa | ISO 527-3 |
| TD, yield, 25 µ m, blow molded film | 18.0 | MPa | ISO 527-3 |
| MD, fracture, 25 µ m, blow molded film | 50.0 | MPa | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 40.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 550 | % | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 700 | % | ISO 527-3 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 80 | g | ISO 7765-1/A |
| tear strength | ISO 6383-2 | ||
| MD，25 µm | 40.0 | kN/m | ISO 6383-2 |
| TD，25 µm | 200.0 | kN/m | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 118 | ℃ | ISO 306/A |
| Melting temperature | 128 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 50 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 14 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 230 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |