| Clearflex FG 306 is a hexene copolymer linear low density polyethylene (C6-LLDPE), additivated with antioxidant, antiblocking and processing aid, suitable for blown film extrusion. Film manufactured with Clearflex FG 306 are characterised by good balance between rigidity, impact resistance and tear resistance (Elmendorf). Main Application Clearflex FG 306 is recommended for the production of heavy duty bags, both in coextrusion and in blend with LDPE.&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,High anti-blocking,Food contact compliance,Inoxidizability,Low density,Good tear strength,Copolymer,Hexene copolymers |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.926 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Self dynamic, blow molded film | > 0.50 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| film thickness | 10 to 50µm | ||
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, 25 µ m, blow molded film | 190 | MPa | ISO 527-3 |
| 1% secant, TD, 25 µ m, blow molded film | 225 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 25 µ m, blow molded film | 12.0 | MPa | ISO 527-3 |
| TD, yield, 25 µ m, blow molded film | 13.0 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 45.0 | MPa | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 36.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 550 | % | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 740 | % | ISO 527-3 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 120 | g | ISO 7765-1/A |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD：25.0 µm | 82.0 | kN/m | ISO 6383-2 |
| TD：25.0 µm | 250.0 | kN/m | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 110 | ℃ | ISO 306/A |
| Melting temperature | 127 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 52 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 13 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 230 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |