| About |
|---|
| Clearflex FG 336 is a hexene copolymer linear low density polyethylene (C6-LLDPE), additivated with antioxidant, slip agent, antiblocking agent and processing aid, suitable for blown film extrusion. Films obtained from Clearflex FG 336 show high rigidity together with optimum Elmendorf tear and impact resistance. Main Application Clearflex FG 336 is recommended for shipping sacks, where the perfect balance between additivation (in terms of slip and antiblocking) and mechanical performances leads to the manufacture of a tough and easy peelable film. Moreover, for its sealing characteristics, together with low temperature mechanical resistance, Clearflex FG 336 is suggested for the production of freezer bags, either in coextrusion and in blend with LDPE.&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,High impact resistance,Smoothness,High anti-blocking,Food contact compliance,Inoxidizability,Low density,Good tear strength,Copolymer,Hexene copolymers |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.926 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Self dynamic, blow molded film | 0.11 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| film thickness | 10 to 50µm | ||
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, 25 µ m, blow molded film | 180 | MPa | ISO 527-3 |
| 1% secant, TD, 25 µ m, blow molded film | 200 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 25 µ m, blow molded film | 12.0 | MPa | ISO 527-3 |
| TD, yield, 25 µ m, blow molded film | 13.0 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 45.0 | MPa | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 36.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 550 | % | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 740 | % | ISO 527-3 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 120 | g | ISO 7765-1/A |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD：25.0 µm | 82.0 | kN/m | ISO 6383-2 |
| TD：25.0 µm | 250.0 | kN/m | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 110 | ℃ | ISO 306/A |
| Melting temperature | 127 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 54 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 13 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 3. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |