Clearflex® FG B3

About
Clearflex FG B3 is a linear low density polyethylene, with antioxidants, slip and antiblocking agents, suitable for blown film technology. The product is characterised by a very low density and a high molecular weight. Films made by Clearflex FG B3 are highly transparent, have a good sealing, even at low temperature, and mechanical properties. It represent the version with slip and antiblock of Clearflex FG B0. Main Application Clearflex FG B3 is recommended for coextrusion to produce lamination film and is used in blend or coextrusion because of its unique properties.&&

About

Clearflex FG B3 is a linear low density polyethylene, with antioxidants, slip and antiblocking agents, suitable for blown film technology. The product is characterised by a very low density and a high molecular weight. Films made by Clearflex FG B3 are highly transparent, have a good sealing, even at low temperature, and mechanical properties. It represent the version with slip and antiblock of Clearflex FG B0. Main Application Clearflex FG B3 is recommended for coextrusion to produce lamination film and is used in blend or coextrusion because of its unique properties.&&

Product Description
Generic	VLDPE
Material Status	Commercial: Active
Features	Good Clarity,Good heat sealing,Smoothness,High anti-blocking,Food contact compliance,Inoxidizability,High molecular weight,Low density,Low temperature heat sealing
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.911	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	0.90	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
friction coefficient
Self dynamic, blow molded film	0.15		ISO 8295

film	Nominal value	Unit	Test method
film thickness	10 to 50µm
Tensile modulus			ISO 527-3
1% secant, MD, blow molded film	90.0	MPa
1% secant, TD, blow molded film	100	MPa
tensile strength			ISO 527-3
MD, yield, blow molded film	7.00	MPa
TD, yield, blow molded film	7.00	MPa
MD, fracture, blow molded film	35.0	MPa
TD, fracture, blow molded film	32.0	MPa
Tensile strain			ISO 527-3
MD, fracture, blow molded film	500	%
TD, fracture, blow molded film	700	%
Drop hammer impact
Blown film	250	g	ISO 7765-1
tear strength			ISO 6383-2
MD	70.0	kN/m
TD	110.0	kN/m

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -70.0	℃	ASTM D746
Vicat Softening Temp	88.0	℃	ISO 306/A
Melting temperature	120	℃	Internal Method

optical performance	Nominal value	Unit	Test method
gloss
45 °, blow molded film	66		ASTM D2457
Haze
Blown film	7.0	%	ISO 14782

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	200 to 230	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.