| Clearflex H&T LGH 108 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion. Films obtained from Clearflex H&T LGH 108 show excellent optical properties, a wide sealing window, both hot tack and heat seal, together with a low sealing initiation temperature (S.I.T.) and outstanding impact, puncture and Elmendorf tear resistance. Main Application Clearflex H&T LGH 108, for its overall characteristics, is the right choice for packaging film applications, bioriented film requiring superior mechanical and optical properties. Moreover, the excellent sealability behaviour together with low gel content makes it ideal for lamination film production.&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good heat sealing,High impact resistance,Optical performance,Low speed solidification point,Food contact compliance,Thermal viscous strength,Inoxidizability,Broad Seal Range,Low density,Good tear strength,Octene copolymer,Copolymer,Puncture Resistant,Low temperature heat sealing |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.917 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.90 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Self dynamic, blow molded film | > 0.50 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| film thickness | 10 to 50µm | ||
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, 25 µ m, blow molded film | 160 | MPa | |
| 1% secant, TD, 25 µ m, blow molded film | 170 | MPa | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 25 µ m, blow molded film | 9.00 | MPa | |
| TD, yield, 25 µ m, blow molded film | 9.00 | MPa | |
| MD, fracture, 25 µ m, blow molded film | 45.0 | MPa | |
| TD, fracture, 25 µ m, blow molded film | 45.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 450 | % | |
| TD, fracture, 25 µ m, blow molded film | 700 | % | |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 400 | g | ISO 7765-1 |
| tear strength | ISO 6383-2 | ||
| MD，25 µm | 130.0 | kN/m | |
| TD，25 µm | 210.0 | kN/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 102 | ℃ | ISO 306/A |
| Melting temperature | 117 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 60 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 9.0 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 230 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |