| About |
|---|
| Clyrell RC124H is a high modified polypropylene random copolymer designed for extrusion applications. Clyrell RC124H exhibits enhanced optical properties. The main applications of Clyrell RC124H are blown film extrusion, sheet extrusion and thermoforming.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good surface appearance,Optical performance |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.2 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 750 | MPa | ISO 527-1-2 |
| Tensile strain | ISO 527-2/50 | ||
| yield | 15 | % | ISO 527-2/50 |
| fracture | 510 | % | ISO 527-2/50 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| MD | 600 | MPa | ASTM D882 |
| MD: 40 µ m, blow molded film | 840 | MPa | ASTM D882 |
| TD: 40 µ m, blow molded film | 860 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| yield | 25.0 | MPa | ISO 527-2/50 |
| MD, yield | 18.0 | MPa | ASTM D882 |
| MD, yield, 40 µ m, blow molded film | 27.0 | MPa | ASTM D882 |
| TD, yield, 40 µ m, blow molded film | 25.0 | MPa | ASTM D882 |
| MD, fracture | 40.0 | MPa | ASTM D882 |
| MD, fracture, 40 µ m, blow molded film | 31.0 | MPa | ASTM D882 |
| TD, fracture, 40 µ m, blow molded film | 27.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, yield, 40 µ m, blow molded film | 9.0 | % | ASTM D882 |
| TD, yield, 40 µ m, blow molded film | 8.0 | % | ASTM D882 |
| MD, fracture | 730 | % | ASTM D882 |
| MD, fracture, 40 µ m, blow molded film | 590 | % | ASTM D882 |
| TD, fracture, 40 µ m, blow molded film | 540 | % | ASTM D882 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 30 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 69.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 122 | ℃ | ISO 306/A50 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D2457 | ||
| 45°，50 µm | 91 | ASTM D2457 | |
| 45 °, 40.0 µ m, blow molded film | 93 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 50 µm | < 1.0 | % | ASTM D1003 |
| 40 µ m, blow molded film | 1.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.98 in/min |
| 3. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |