| Cogegum® XLPO-HFFR – Crosslinkable Halogen Free Fire Retardant compound Silane grafted compound moisture curable by addition of a catalyst masterbatch (Sioplas® method). It consists of a polyolefin base containing a fire retardant system that contributes to give the cable self-extinguish properties without halogenidric acids evolution, toxic and corrosive gases and dark smoke emission. This material complies with RoHS requirements. Standard complying EN 50363-0 G7 and G10; VDE 0250/503 HI3; VDE 0266 HXI1 and HXI2; IEC 60092/360 EPR, HEPR, XLPE and HF 90; Cenelec HD 624.6&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Negative |
| Features | Low smoke,Crosslinked,Halogen free,Flame Characteristics,Low toxicity,Self-extinguishing |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 7.3 | g/10min | Internal Method |
| Water absorption rate | |||
| 100℃，24hr | < 4.00 | mg/cm² | IEC 60811 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Changes in mechanical properties after hot air aging test, 150 ℃, 168 hr | IEC 60811 | ||
| The rate of change in tensile strength | 13 | % | IEC 60811 |
| Change in tensile elongation | -5 | % | IEC 60811 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| impact test | |||
| thermosetting | IEC 60811 | ||
| Elongation at break under load: 250 ℃ | 50 | % | IEC 60811 |
| Maximum permanent elongation after cooling: 250 ℃ | 0.0 | % | IEC 60811 |
| Bending test | |||
| -15℃ | No cracks | IEC 60811 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | IEC 60502 | ||
| 20 ℃ | 1.6E+15 | ohms·cm | IEC 60502 |
| 90 ℃ | 1.4E+14 | ohms·cm | IEC 60502 |
| Insulation resistance constant | IEC 60502 | ||
| 20℃ | 6000 | Mohms·km | IEC 60502 |
| 90℃ | 500 | Mohms·km | IEC 60502 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 27 | % | ASTM D2863 |
| Discharge of halogenated acid | < 0.10 | % | IEC 60754-1 |
| Temperature index | |||
| burning | 300 | ℃ | NES 715 |
| Corrosive gases in flue gas | IEC 60754-2 | ||
| Conductivity | < 10.0 | µS/mm | IEC 60754-2 |
| pH | > 4.30 | IEC 60754-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 41 | ISO 868 | |
| Tensile modulus | 7.00 | MPa | IEC 60811 |
| tensile strength | |||
| fracture | 12.3 | MPa | IEC 60811 |
| Tensile strain | |||
| fracture | 260 | % | IEC 60811 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 130 to 150 | °C | |
| Barrel 2 zone temperature | 130 to 150 | °C | |
| Barrel 3 zone temperature | 140 to 160 | °C | |
| Barrel 4 zone temperature | 140 to 160 | °C | |
| Ring temperature | 140 to 160 | °C | |
| Head temperature | 140 to 160 | °C | |
| Nozzle temperature | 160 to 180 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |