| About |
|---|
| Complet® LCF20-LGF20-PA66 is a Polyamide 66 (Nylon 66) product filled with 20% long carbon fiber and 20% long glass fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: rohs compliant.&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 24100 | MPa | ASTM D638 |
| tensile strength | 284 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.0 to 2.0 | % | ASTM D638 |
| Bending modulus | 17900 | MPa | ASTM D790 |
| bending strength | 405 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 270 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 1000 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 254 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 85 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.18 | % | |
| Proposed maximum recycled material ratio | 5 | % | |
| Barrel rear temperature | 282 to 299 | °C | |
| Barrel middle temperature | 288 to 304 | °C | |
| Barrel front temperature | 293 to 310 | °C | |
| Nozzle temperature | 288 to 304 | °C | |
| Processing (melt) temperature | 293 to 310 | °C | |
| Mold temperature | 93 | °C | |
| Back pressure | 0.172 to 0.345 | MPa | |
| Screw speed | 30 to 50 | rpm | |
| Cushion | 6.35 | mm | |
| Screw length to diameter ratio | 18.0:1.0 to 20.0:1.0 | ||
| Screw compression ratio | 2.0 : 1.0 to 3.0 : 1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |