| CONATHANE EN-2550 is a two-part, filled polyurethane resin system formulated for casting high-voltage transformers and potting or encapsulating electronic devices. The system features good handling properties at room temperature, good working life, and minimum processing hazards. CONATHANE EN-2550 can be cured at room or elevated temperatures without the formation of voids. The cured compound has excellent water resistance, and is resistant to thermal shock. Other beneficial characteristics of this system include low exotherm, low stresses during cure, low shrinkage, and very good electrical properties.&& |
| Product Description | |
|---|---|
| Supplier | Cytec Industries |
| Generic | PUR |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Electrical Properties,Low Exotherm,Antimicrobial properties,Low contractility,Good thermal shock resistance,V-0 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.23 | g/cm³ | |
| — | 1.52 | g/cm³ | |
| Water absorption rate | |||
| 25 ℃, 24 hours, in water | 0.075 | % | |
| 7days | 0.19 | % | |
| 25 ℃, 7 days, in water | 1.5 | % | |
| Solid content | |||
| — | 100 | % | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 41.2 | kN/m |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | |||
| — | 6.1E+17 | ohms | |
| — | 1.5E+14 | ohms | |
| — | 7.8E+11 | ohms | |
| Volume resistivity | |||
| 25 ℃ | 2.1E+14 | ohms·cm | |
| 60 ℃ | 1.1E+13 | ohms·cm | |
| 120 ℃ | 1.4E+11 | ohms·cm | |
| Dielectric strength | |||
| 0.406 mm | 43 | kV/mm | |
| 0.813 mm | 33 | kV/mm | |
| 1.57 mm | 21 | kV/mm | |
| Dielectric constant | |||
| 25 ℃，100 Hz | 4.38 | ||
| 25 ℃，1 kHz | 4.13 | ||
| 25 ℃，1 MHz | 3.81 | ||
| Dissipation factor | |||
| 25℃，100 Hz | 0.096 | ||
| 25℃，1 kHz | 0.034 | ||
| 25℃，1 MHz | 0.020 | ||
| Arc resistance | > 120 | sec | |
| insulation resistance | |||
| 25℃ | 3.0E+13 | ohms | |
| 60℃ | 1.0E+11 | ohms | |
| 120℃ | 1.2E+10 | ohms |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| 25℃ | 150 | cP | |
| 25℃ | 17000 | cP | |
| 25℃ | 3000 | cP | |
| 40℃ | 1200 | cP |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Cold and hot shock test -10 cycles, -65 ℃ to 130 ℃ | passes | ||
| Working period | |||
| 234 gm mass to 100000 cps，25℃ | 53.0 | min | |
| Antifungal activity | Non-nutrient |
| Cured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear Shrinkage | 0.58 | % |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 50 | ||
| tensile strength | 12.4 | MPa | |
| Tensile strain | |||
| fracture | 630 | % |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD | 1.6E-4 | 1/℃ | |
| Thermal conductivity coefficient | 0.33 | W/m/K | |
| Thermosetting components | |||
| resin | 按重量计算的混合比: 17 | ||
| Hardening method | 按重量计算的混合比: 100 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Resin |
| 3. Hardener |
| 4. 90°C |
| 5. 60°C |
| 6. 25°C |
| 7. Mixed |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |