| DESCRIPTION Cosmic D62 / 6130F is a long glass fiber filled, flame retardant, general purpose diallyl ortho phthalate molding compound which is supplied in a flake form. It can be easily molded in compression or transfer equipment and can be readily preformed for ease in handling. It has passed NASA outgassing tests. FEATURES D62 / 6130F is particularly suited to applications requiring resistance to elevated temperatures and high humidity. It has a high impact strength, excellent compressive and flexural strength, and very good electrical properties. APPLICATIONS Structural parts, housings, terminals, insulators and other applications requiring flame resistance or strength.&& |
| Product Description | |
|---|---|
| Generic | DAP增塑剂 |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good Electrical Properties,Flame Characteristics,High Heat Resistance,Moisture resistance,Good compressive strength,V-0 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.82 | g/cm³ | |
| Shrinkage rate | 6.0 | ||
| Shrinkage rate | |||
| MD | 0.10 to 0.40 | % | |
| dimensional stability | < 0.010 | % | |
| Water absorption rate | |||
| Equilibrium, 50 ℃ | 0.30 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 41.4 to 68.9 | MPa | |
| bending strength | 89.6 to 117 | MPa | |
| compressive strength | 165 to 207 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 160 to 320 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD：-40~100℃ | 2.4E-5 | 1/℃ | |
| Hot deformation temperature | 260 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | |||
| — | > 1.0E+16 | ohms | |
| — | 2.6E+10 | ohms | |
| Volume resistivity | |||
| — | > 1.0E+16 | ohms·cm | |
| — | 2.0E+10 | ohms·cm | |
| Dielectric strength | |||
| Dry | 16 | kV/mm | |
| moist | 14 | kV/mm | |
| Dielectric constant | |||
| 1 kHz | 4.20 | ||
| 1 kHz | 4.40 | ||
| 1 MHz | 4.00 | ||
| 1 MHz | 4.20 | ||
| Dissipation factor | |||
| 1 kHz | 6.0E-3 | ||
| 1 kHz | 9.0E-3 | ||
| 1 MHz | 0.014 | ||
| 1 MHz | 0.016 | ||
| Arc resistance | 180 | sec | |
| breakdown voltage | |||
| Dry | 62000 | V | |
| Wet | 60000 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Water Extract Conductivity | 30.0 | µS/cm |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 135 to 190 | °C | |
| Injection pressure | 3.45 to 55.2 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 48 hrs |
| 3. 30 days @ 100% RH @ 70°C |
| 4. As Is |
| 5. Method B (Step-by-Step) |
| 6. Wet |
| 7. Dry |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |