| About |
|---|
| COSMOPLENE AS164 is melt stable, high stiffness, super high impact PP copolymer manufactured by gas phase process licensed from Sumitomo Chemical Co. Japan. COSMOPLENE AS164 is suitable for products such as injection for seat bottom, extrusion for corrugated sheet, pipe and fittings, bicycle rims, blow bottle etc.&& |
| Product Description | |
|---|---|
| Supplier | TPC |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Impact copolymer,Higher melt stability |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D792 |
| Melt Flow Rate | 1.2 | g/10min | ASTM D1238 |
| Shrinkage rate | Internal Method | ||
| MD：2.0 mm | 1.5 | % | Internal Method |
| TD：2.0 mm | 1.4 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃ | 62 | J/m | ASTM D256 |
| 23℃ | 490 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 117 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 86 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| yield | 28.5 | MPa | ASTM D638 |
| fracture | 26.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 500 | % | ASTM D638 |
| Bending modulus | 1100 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 190 to 230 | °C | |
| Barrel middle temperature | 190 to 230 | °C | |
| Barrel front temperature | 190 to 230 | °C | |
| Mold temperature | 30 | °C | |
| Injection pressure | 6.86 | MPa | |
| Clamping force | 0.98 | kN/cm² | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |