| About |
|---|
| COSMOPLENE AW864 is high impact PP copolymer manufactured by gas phase process licensed from Sumitomo Chemical Co. Japan. COSMOPLENE AW864 is medium flow, high stiffness, high impact copolymer grade which contains anti-static agent and UV stabilizers. COSMOPLENE AW864 is specially designed for crates, washing machine parts and automotive parts.&& |
| Product Description | |
|---|---|
| Supplier | TPC |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,High impact resistance,High liquidity,Moderate liquidity,Antistatic property,Impact copolymer,HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D792 |
| Melt Flow Rate | 9.0 | g/10min | ASTM D1238 |
| Shrinkage rate | Internal Method | ||
| MD：2.0 mm | 1.6 | % | Internal Method |
| TD：2.0 mm | 1.7 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃ | 45 | J/m | ASTM D256 |
| 23℃ | 92 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 124 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Weathering resistance | |||
| 63℃ | 1.4 | month | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 91 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| yield | 27.5 | MPa | ASTM D638 |
| fracture | 23.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 300 | % | ASTM D638 |
| Bending modulus | 1290 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 190 to 230 | °C | |
| Barrel middle temperature | 190 to 230 | °C | |
| Barrel front temperature | 190 to 230 | °C | |
| Mold temperature | 30 | °C | |
| Injection pressure | 6.86 | MPa | |
| Clamping force | 0.98 | kN/cm² | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. SWOM |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |