| About |
|---|
| COSMOPLENE FS6612L is Polypropylene Terpolymer product designed for double bubble process with low heat temperature, high transparency and surfact gloss. COSMOPLENE FS6612L is suitable for skin layer when coextruded with LLDPE as core layer for shrink film application. FS6612L contains Antiblocking agent and slip agent.&& |
| Product Description | |
|---|---|
| Supplier | TPC |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good surface appearance,Smoothness,High anti-blocking,Terpolymer,Low temperature heat sealing |
| Availabilitys | Asia Pacific |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D792 |
| Melt Flow Rate | 5.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 44.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 880 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 760 | MPa | ASTM D747 |
| friction coefficient | |||
| With oneself – static | 0.40 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 30 | µm | |
| Secant modulus | Internal Method | ||
| MD：30 µm | 360 | MPa | Internal Method |
| TD：30 µm | 370 | MPa | Internal Method |
| Initial sealing temperature | |||
| 30 µm | 115 | ℃ | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 128 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 30 µm | 150 | ASTM D2457 | |
| Haze | |||
| 30 µm | 1.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 250 | °C | |
| Traction roller | 26 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |