| About |
|---|
| Prime ABS, High Impact, Natural&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 3.7 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 220℃，10 kg | 15.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.80 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2070 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| yield | 41.4 | MPa | ASTM D638 |
| fracture | 31.7 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| yield | 2.1 | % | ASTM D638 |
| fracture | 26 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 2140 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 68.3 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 370 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | 31.1 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 97.2 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 82.2 | ℃ | ASTM D648 |
| Vicat Softening Temp | 98.9 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 8.8E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 8.8E-5 | 1/℃ | ASTM E831 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 to 93 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 188 to 210 | °C | |
| Barrel middle temperature | 204 to 227 | °C | |
| Barrel front temperature | 216 to 238 | °C | |
| Nozzle temperature | 218 to 260 | °C | |
| Mold temperature | 49 to 71 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |