| About |
|---|
| Product Description | |
|---|---|
| Generic | PETG |
| Material Status | Commercial: Negative |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | ASTM D792 | |
| Rockwell hardness | 119 | R Scale | ASTM D785 |
| Water absorption rate | 0.15 | % | ASTM D570 |
| elongation | |||
| yield | 5.1 | % | ASTM D638 |
| fracture | 88 | % | ASTM D638 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 51.0 | MPa | ASTM D638 |
| fracture | 29.2 | MPa | ASTM D638 |
| bending strength | 70.8 | MPa | ASTM D790 |
| Bending modulus | 2090 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 23℃ | 51 | j/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 66psi | 76.2 | ℃ | ASTM D648 |
| 264psi | 66.2 | ℃ | ASTM D648 |
| Vicat Softening Temp | 79.1 | ℃ | ASTM D1525 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.05E+16 | ohm | ASTM D257 |
| Volume resistivity | 1.23E+16 | ohm·cm | ASTM D257 |
| Dielectric strength | 15.83 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 kHz | 2.32 | ASTM D150 | |
| 1 MHz | 2.13 | ASTM D150 | |
| Dissipation factor | |||
| 1 kHz | 0.0058 | ASTM D150 | |
| 1 MHz | 0.0246 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| UL flame retardant rating | |||
| 1.50mm | HB | UL 94 | |
| 3.20mm | V-2 | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | 1.1 | % | ASTM D1003 |
| Transmittance | 90.2 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |