| About |
|---|
| Crastin® FGS600F40 BK594 is a THERMOPLASTIC POLYESTER RESIN product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2700 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 58.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 10 | % | ISO 527-2 |
| Nominal tensile fracture strain | 20 | % | ISO 527-2 |
| Bending modulus | 2500 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 57.0 | ℃ | ISO 75-2/A |
| Glass transition temperature | 55.0 | ℃ | ISO 11357-2 |
| Melting temperature | 225 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 1.1E-4 | 1/℃ | |
| TD | 1.2E-4 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 1 mm | < 100 | mm/min | ISO 3795 |
| Flammability level | |||
| 1.5 mm | HB | IEC 60695-11-10, -20 | |
| Extreme oxygen index | 22 | % | ISO 4589-2 |
| FMVSS flame retardant rating | B | FMVSS 302 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 250℃，2.16kg | 36 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 1.8 | % | |
| MD | 1.8 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃, 2.00 mm | 0.40 | % | |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 0.20 | % | |
| Melt density | 1.11 | g/cm³ | |
| Ejection temperature | 170 | ℃ | |
| Specific Heat Capacity of Melt | 2110 | J/kg/℃ | |
| Thermal Conductivity of Melt | 0.21 | W/m/K |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Melt Temperature, Optimum | 250 | °C | |
| Mold temperature | 30 to 130 | °C | |
| Mold Temperature, Optimum | 80 | °C | |
| Hold pressure | 60.0 | MPa | |
| Back Pressure | As low as possible | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 3. From Crastin® S600F40 NC010 |
| 4. FMVSS 302 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |