| About |
|---|
| 20% Glass Reinforced, Flame Retardant, Polybutylene Terephthalate&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 8300 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 110 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.8 | % | ISO 527-2 |
| bending strength | 165 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.6 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 50 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 200 | ℃ | ISO 75-2/A |
| Melting temperature | 225 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 225 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| Flammability level | IEC 60695-11-10, -20 | ||
| 0.75 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | IEC 60695-11-10, -20 | |
| Extreme oxygen index | 32 | % | ISO 4589-2 |
| FMVSS flame retardant rating | DNI | FMVSS 302 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.5 | % | ISO 294-4 |
| TD | 1.2 | % | ISO 294-4 |
| MD | 0.50 | % | ISO 294-4 |
| MD | 0.60 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃, 2.00 mm | 0.32 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 0.13 | % | ISO 62 |
| Ejection temperature | 170 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Melt Temperature, Optimum | 250 | °C | |
| Mold temperature | 30 to 130 | °C | |
| Mold Temperature, Optimum | 80 | °C | |
| Hold pressure | 60.0 | MPa | |
| Back pressure | As low as possible | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Annealed |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |