| About |
|---|
| Unreinforced, Flame Retardant, UV Stabilized, Polybutylene Terephthalate&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Flame Characteristics,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2200 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 41.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 9.0 | % | ISO 527-2 |
| Nominal tensile fracture strain | 45 | % | ISO 527-2 |
| Bending modulus | 2100 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40℃ | 10 | kJ/m² | ISO 179/1eA |
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 65 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -40℃ | 350 | kJ/m² | ISO 179/1eU |
| -30℃ | 350 | kJ/m² | ISO 179/1eU |
| 23℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | 10 | kJ/m² | ISO 180-1A |
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 70 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -40℃ | 220 | kJ/m² | ISO 180/1U |
| -30℃ | 220 | kJ/m² | ISO 180/1U |
| 23℃ | No Break | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 55.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 125 | ℃ | ISO 75-2/B |
| Melting temperature | 225 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 1.9E-4 | 1/℃ | ISO 11359-2 |
| MD | 1.9E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 36 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 3.50 | IEC 60250 | |
| 1 MHz | 3.40 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 1.1E-3 | IEC 60250 | |
| 1 MHz | 0.024 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.90 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| Flammability level | IEC 60695-11-10, -20 | ||
| 0.9 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | IEC 60695-11-10, -20 | |
| Extreme oxygen index | 27 | % | ISO 4589-2 |
| FMVSS flame retardant rating | DNI | FMVSS 302 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 250℃，5.0kg | 3.0 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.6 | % | ISO 294-4 |
| MD | 2.0 | % | ISO 294-4 |
| Melt density | 1.17 | g/cm³ | |
| Ejection temperature | 170 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Melt Temperature, Optimum | 250 | °C | |
| Mold temperature | 30 to 130 | °C | |
| Mold Temperature, Optimum | 80 | °C | |
| Hold pressure | 60.0 | MPa | |
| Back pressure | As low as possible | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |