| About |
|---|
| 66% Fluorine copolymers formulated for injection molding. GP-LV compounds also exhibit the improved hot tear resistance of their higher viscosity counterparts.&& |
| Product Description | |
|---|---|
| Generic | 氟橡胶 |
| Material Status | Commercial: Active |
| Features | Low Viscosity,Copolymer |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.83 | g/cm³ | |
| Mooney viscosity | |||
| ML 1+10，121℃ | 75 | MU | |
| Fluorine content | 66 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 91 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 13.2 | MPa | |
| 100% strain | 9.93 | MPa | |
| Tensile strain | |||
| fracture | 140 | % | |
| Compression deformation | |||
| 200℃，22 hr | 30 | % |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Plied discs |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |