| About |
|---|
| The LS compounds are designed to give part shrinkage (out of the mold) and post-curing operation comparable to a nitrile or similar elastomer. In most cases, tooling changes are not required when switching over to an LS compound. NPC indicates no post cure required to achieve high tensile and modulus values with good compression set and aging characteristics. FKHT is a high temperature resistant, low compression set compound. FKX is a high viscosity, high green strength, black fluorocarbon compound formulated for HAV and / or salt bath curing of O-ring cord and extruded profiles.&& |
| Product Description | |
|---|---|
| Generic | 氟橡胶 |
| Material Status | Commercial: Active |
| Features | Good Tensile Strength |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.86 | g/cm³ | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 79 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 15.5 | MPa | |
| 100% strain | 8.27 | MPa | |
| Tensile strain | |||
| fracture | 210 | % | |
| Compression deformation | |||
| 200℃，22 hr | 20 | % |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Plied discs |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |