| About |
|---|
| Crystal Clear® 200, 202, 204 and 206 are water white clear and made specifically for applications that require clarity. These rigid urethane casting resins differ only in working and demold times. Low viscosity ensures easy mixing and pouring. Crystal Clear® resins cure at room temperature* with negligible shrinkage. Cured castings are UV Resistant and are not brittle. Vibrant colors and color effects are achieved by adding pigment dispersions. Applications include encapsulation, making prototype models, lenses, sculpture reproductions, decorative cast pieces, jewelry, prototype models, special effects and props. Crystal Clear® 220 and 221 are harder, heat cured products that offer advantages over these room temp. cure products. A separate tech bulletin is available for Crystal Clear® 220 and 221 at www.smooth-on.com. CAUTION: NOT FOR HOME USE. THIS PRODUCT IS FOR INDUSTRIAL USE ONLY. Proper ventilation, A NIOSH Approved Respirator and Protective Clothing (gloves and long sleeves) are required to minimize the risk of inhalation and dermal sensitization. If breathing is affected or a dermal rash develops, immediately cease using this product and seek medical attention. Read SDS before using.&& |
| Product Description | |
|---|---|
| Material Status | Commercial: Active |
| Features | Low Viscosity,Good coloring,Low contractility,Good Clarity,Good Rigidity,Weather resistance is good |
| Availabilitys | Europe,North America,Asia Pacific,Latin America,Africa & Middle East |
| Process Methods | casting |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ASTM D1475 |
| Specific volume | 0.965 | cm³/g | ASTM D1475 |
| Molding shrinkage | |||
| MD | 1.3 | % | ASTM D2566 |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| stripping time | |||
| 23℃ | 90 | min |
| Supplementary Information | Nominal value | Unit | Test method |
|---|---|---|---|
| Mixing ratio | 100A:90B by weight |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 80 | ASTM D2240 | |
| Tensile Modulus | 595 | MPa | ASTM D638 |
| Tensile Strength | 24.1 | MPa | ASTM D638 |
| Tensile Strain | |||
| fracture | 10 | % | ASTM D638 |
| Flexural Modulus | 1260 | MPa | ASTM D790 |
| Flexural Strength | 37.2 | MPa | ASTM D790 |
| Compressive Modulus | 303 | MPa | ASTM D695 |
| Compressive Strength | 29.0 | MPa | ASTM D695 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 48.9 | ℃ | ASTM D648 |
| storage stability | 9.0 | min |
| OPTICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive Index | |||
| 20℃ | 1.49888 | % | |
| 25℃ | 1.49893 | % |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric Strength | 10.24 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 100Hz | 3.36 | ASTM D150 | |
| 1 KHz | 3.34 | ASTM D150 | |
| Dissipation Factor | |||
| 100Hz | 0 | ASTM D150 | |
| 1 KHz | 0.01 | ASTM D150 | |
| Volume Resistance | 1.4E15 | ohm·cm | ASTM D257 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20°C |
| 3. Cure Time |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |