| Product Description | |
|---|---|
| Material Status | Commercial: Active |
| Features | Good Clarity,Low contractility,Good Rigidity,Good coloring,Weather resistance is good,Low Viscosity |
| Availabilitys | Africa & Middle East ,North America,Europe,Asia Pacific,Latin America |
| Process Methods | casting |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ASTM D1475 |
| Specific volume | 0.965 | cm³/g | ASTM D1475 |
| Molding shrinkage | |||
| MD | 0.20 | % | ASTM D2566 |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| stripping time | |||
| 23℃ | 7200 | min |
| Supplementary Information | Nominal value | Unit | Test method |
|---|---|---|---|
| Mixing ratio | 100A:90B by weight |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 80 | ASTM D2240 | |
| Tensile Modulus | 505 | MPa | ASTM D638 |
| Tensile Strength | 17.2 | MPa | ASTM D638 |
| Tensile Strain | |||
| fracture | 10 | % | ASTM D638 |
| Flexural Modulus | 138 | MPa | ASTM D790 |
| Flexural Strength | 73.4 | MPa | ASTM D790 |
| Compressive Modulus | 276 | MPa | ASTM D695 |
| Compressive Strength | 44.0 | MPa | ASTM D695 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 48.9 | ℃ | ASTM D648 |
| storage stability | 180 | min |
| OPTICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive Index | |||
| 20℃ | 1.49962 | % | |
| 25℃ | 1.49894 | % |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric Strength | 10.24 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 100 Hz | 3.36 | ASTM D150 | |
| 1 KHz | 3.34 | ASTM D150 | |
| Dissipation Factor | |||
| 100 Hz | 0 | ASTM D150 | |
| 1 KHz | 0.01 | ASTM D150 | |
| Volume Resistance | 1.4E15 | ohm·cm | ASTM D257 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |