| About |
|---|
| A new generation thermoplastic composite Curv™ is a novel material made from Polypropylene that combines ther versatility and recyclability of a 100% thermoplastic with the high performance of a fiber reinforced composite. High stiffness, high tensile strength and outstanding impact resistance at low density are the remarkable properties of these materials. Product: Polypropylene/Polypropylene Thermoformable Composite Sheet Dimensions: Thickness: 0.3 to 3.0 mm Available Width: up to 1360 mm Standard Length: Any lenght up to 3 meters, thinner sheets available on roll Color: standard – black, other colors subejct to minimum volume&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Renewable resources,Good Tensile Strength |
| Availabilitys | North America |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.920 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，24hr | < 0.10 | % | DIN 53495 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | 3500 | MPa | ISO 178 |
| compressive strength | 300 | MPa | ISO 604 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Membrane puncture strength | |||
| 2100 µm | 40.0 | J | ISO 6603-2 |
| Tensile modulus | ISO 527-3 | ||
| MD | 4200 | MPa | ISO 527-3 |
| TD | 4200 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD | 120 | MPa | ISO 527-3 |
| TD | 120 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture | 20 | % | ISO 527-3 |
| TD, fracture | 20 | % | ISO 527-3 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -40℃ | 无断裂 | ISO 179 | |
| 20℃ | 120 | kJ/m² | ISO 179/2B |
| 23℃ | > 250 | kJ/m² | ISO 179/2 |
| Impact strength of cantilever beam notch | ISO 180/B | ||
| -40℃ | 600 | kJ/m² | ISO 180-B |
| 20℃ | 400 | kJ/m² | ISO 180-B |
| Tensile impact strength | |||
| 20℃，2.10 mm | 1000 | kJ/m² | ISO 8256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 102 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 160 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 175 | ℃ | ISO 306/B |
| Linear coefficient of thermal expansion | |||
| MD：20~80℃ | 6.8E-5 | 1/℃ | DIN 53752 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| building materials | B2 | DIN 4102 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. TD, flat wise |
| 3. flat wise |
| 4. 20°C, 52 J |
| 5. TD, 52 J |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |