| Automotive. High heat resistance, low gloss, color concentratable for interior applications. Natural only.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,Low Gloss,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2280 | MPa | ASTM D638 |
| Tensile modulus | 2930 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 53.0 | MPa | ASTM D638 |
| yield | 43.0 | MPa | ISO 527-2/50 |
| Bending modulus | 2030 | MPa | ISO 178 |
| 50 mm span | 2460 | MPa | ASTM D790 |
| bending strength | 67.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 81.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 7.2 | kJ/m² | ISO 179/1eA |
| 23℃ | 13 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 290 | J/m | ASTM D256 |
| -30℃ | 7.0 | kJ/m² | ISO 180-1A |
| 23℃ | 13 | kJ/m² | ISO 180-1A |
| Drop hammer impact | |||
| 23℃ | 35.0 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 83.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 81.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 95.0 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 92.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 98.0 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：-40~60℃ | 1.4E-4 | 1/℃ | ASTM E831 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, no texture | 25 | ASTM D523 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 6.0 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 14 | g/10min | ISO 1133 |
| Spiral flow length | 73.7 | cm | Internal Method |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.80 | % | Internal Method |
| Apparent viscosity of melt | |||
| 260℃，1000 sec^-1 | 163 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 88 to 93 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.010 | % | |
| Recommended injection volume | 50 to 70 | % | |
| Barrel rear temperature | 193 to 238 | °C | |
| Barrel middle temperature | 210 to 249 | °C | |
| Barrel front temperature | 221 to 254 | °C | |
| Nozzle temperature | 232 to 274 | °C | |
| Processing (melt) temperature | 232 to 274 | °C | |
| Mold temperature | 49 to 82 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Melt Temperature: 500°F |
| 3. 10 ips, 3.175 x 1524 mm |
| 4. 0.20 in/min |
| 5. Type I, 0.20 in/min |
| 6. 0.051 in/min |
| 7. 0.079 in/min |
| 8. Yield |
| 9. 80*10*4 sp=62mm |
| 10. 80*10*4 |
| 11. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |