| CYCOLAC DL100 is a high heat, high impact, low emissions ABS/PC blend.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,High Heat Resistance,Low odor,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 7.0 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 260℃，5 kg | 8.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 14 | kJ/m² | ISO 179/1eA |
| 23℃ | 34 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃ | 700 | J/m | ASTM D256 |
| 23℃，6.4mm | 550 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 15 | kJ/m² | ISO 180-1A |
| 23℃ | 35 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 100 mm span | 87.0 | ℃ | ISO 75-2/Ae |
| 0.45 MPa, unannealed, 3.2 mm | 105 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span | 104 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.2 mm | 88.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 90.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 105 | ℃ | ISO 306 |
| B120 | 107 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：23~60℃ | 9.8E-5 | 1/℃ | ISO 11359-2 |
| MD：23~60℃ | 9.8E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | |||
| Electrical performance | 60.0 | ℃ | UL 746 |
| Strength mechanical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2240 | MPa | ASTM D638 |
| Tensile modulus | 2200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 44.0 | MPa | ASTM D638 |
| yield | 46.0 | MPa | ISO 527-2/5 |
| yield | 45.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 90 | % | ASTM D638 |
| fracture | 60 | % | ISO 527-2/5 |
| fracture | 10 | % | ISO 527-2/50 |
| Bending modulus | 2260 | MPa | ISO 178 |
| bending strength | 69.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 104 | ASTM D785 | |
| Ball hardness | |||
| H358/30 | 91.0 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 230 to 260 | °C | |
| Barrel middle temperature | 250 to 280 | °C | |
| Barrel front temperature | 250 to 280 | °C | |
| Nozzle temperature | 245 to 275 | °C | |
| Processing (melt) temperature | 250 to 280 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.079 in/min |
| 4. Yield |
| 5. 80*10*4 sp=62mm |
| 6. 80*10*4 |
| 7. 120*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |