| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | ASTM D792 | |
| Shrinkage rate | |||
| MD | 0.4~0.6 | % | Internal Method |
| Melt Flow Rate | |||
| 220℃，10.0kg | 18 | g/10min | ASTM D1238 |
| 230℃，3.80kg | 6 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 47 | MPa | ASTM D638 |
| Tensile stress (fracture) | 25 | % | ASTM D 638 |
| Tensile modulus | 2250 | MPa | ASTM D638 |
| bending strength | |||
| yield | 88 | MPa | ASTM D790 |
| Bending modulus | 2620 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 113 | ASTM D785 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa，3.2 mm | 96 | ℃ | ASTM D648 |
| 1.8 MPa，3.2 mm | 83 | ℃ | ASTM D648 |
| 0.45 MPa，6.4 mm | 98 | ℃ | ASTM D648 |
| Linear expansion coefficient (-30 ℃~30 ℃) | |||
| MD | 6.48×10^-5 | 1/℃ | ASTM E 831 |
| Relative temperature index | |||
| Electrical performance | 60 | ℃ | UL 746B |
| Impact mechanical performance | 60 | ℃ | UL 746B |
| Non mechanical impact performance | 60 | ℃ | UL 746B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 320 | J/m | ASTM D256 |
| -40℃ | 53 | J/m | ASTM D256 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | |||
| Tungsten wire | 6 | PLC Code | ASTM D495 |
| High voltage arc marking rate {PLC} | 3 | PLC Code | UL 746A |
| High current arc ignition, surface {PLC} | 0 | PLC Code | UL 746A |
| Compared to the leakage tracing index | 0 | PLC Code | UL 746A |
| Compared to the leakage tracing index | 0 | PLC Code | UL 746A |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Dry conditions | Nominal value | Unit | Test method |
| Melt Temperature | 230~275 | ℃ | |
| Nozzle temperature | 230~275 | ℃ | |
| Front temperature | 230~2500 | ℃ | |
| Mid section temperature | 225~240 | ℃ | |
| Post stage temperature | 200~210 | ℃ | |
| Mold temperature | 40~80 | ℃ | |
| Back pressure | 0.3~0.7 | MPa | |
| Screw speed | 30~60 | rpm | |
| Shoot to cylinder size | 50~70 | % | |
| Depth of exhaust groove | 0.038~0.051 | mm | |
| drying temperature | 90~95 | ℃ | |
| drying temperature | 90~95 | ℃ | |
| Drying time | 2~4 | hrs | |
| Drying time (cumulative) | 8 | hrs | |
| Maximum moisture content | 0.01 | % | |
| Drying time | 2~4 | hrs | |
| Drying time (cumulative) | 8 | hrs | |
| Maximum moisture content | 0.01 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |